| Certification: | Factory Certification |
|---|---|
| Type: | Moly Disilicide |
| Material: | Moly Disilicide |
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make at Made-in-china.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
MoSi2 heating element is a kind of resistance heating element basically made of high pure Molyndenum Disilicide. In oxidizing atmosphere, a layer of compact quartz protective film is formed on the surface of Mosi2 element owing to the high-temperature combustion, which prevent Mosi2 from continuously oxidizing. In oxidizing atmosphere, its max temperature can reach 1800C, and its applicable temperature is 500-1700C. According to shape, it can be divide into "pole" "U" "W". Special shape such as right angle shape and bend angle shape can be produced according to customer's request.
Silicon molybdenum rod electric heating element products are widely used in metallurgy, Research and production of steelmaking, glass, ceramics, refractory materials, crystals, electronic components, and semiconductor materials manufacturing and other fields, especially for high-performance precision ceramics, high-grade intraocular lenses, precision structural cermets Production of porcelain, glass fiber, optical fiber and high-grade alloy steel.
Physical Properties
| Volume Density | Bend Strength | Vichers-hardness | Porosity Rate | Water Absortion | Hot Extensibility |
| 5.5-5.6 kg/cm3 | 15-25g/cm2 | (HV)570kg/mm2 | 7.4% | 1.2% | 4% |
Chemical Properties
Oxygen-resistance under high temperature: in oxidizing atmosphere, a layer of compact quartz (SiO2) protective film is formed on the surface of element owing to the high-temperature combustion, which prevent Mosi from continuously oxidizing. When the element temperature is higher than 1700C, the SiO2 protective film will be fused because fused because its fusing point is 1710C and the SiO2 is fused into molten drops owing to the action of its surface extension, which cause losing its protective ability. In the oxidizing atmosphere, when the element is contiguously used, the protective film forms again.
It should be pointed out that element cannot be used for rather long time in 400-700C. Otherwise, it will be powdered owing to the strong oxidizing action in low temperature.
The max temperature of elements in different atmosphere
| Atmosphere | Max. element temperature | ||
| Mingxin MX1700 | Mingxin MX1800 | ||
| Air | 1700ºC | 1800ºC | |
| Nitrogen | 1600ºC | 1700ºC | |
| Argon, Helium | 1600ºC | 1700ºC | |
| Hydrogen | 1100-14550ºC | 1100-1450ºC | |
| N2/H2 95/5% | 1250-1600ºC | 1250-1600ºC | |
| General applications | Heattreatment Forging Sintering Glass melting Refing radiant tubes |
Laboratory furnaces Testing equipment High temperature sintering production furnace |
|
Recommend surface load
| Recommend surface load | |||||
| Furnace Temperature (ºC) | 1400 | 1500 | 1600 | 1650 | 1700 |
| Surface load of Hot zone(w/cm2) | <18 | <15 | <12 | <10 | <8 |