Type: | Moly Disilicide |
---|---|
Material: | Moly Disilicide |
Form: | Rod |
Shape: | Rod |
Quality: | Super |
Price: | Good |
Samples: |
---|
Suppliers with verified business licenses
Description
MoSi2 heating element is a kind of resistance heating element basically made of high pure Molyndenum Disilicide. In oxidizing atmosphere, a layer of compact quartz protective film is formed on the surface of Mosi2 element owing to the high-temperature combustion, which prevent Mosi2 from continuously oxidizing. In oxidizing atmosphere, its max temperature can reach 1800C, and its applicable temperature is 500-1700C. According to shape, it can be divide into "pole" "U" "W". Special shape such as right angle shape and bend angle shape can be produced according to customer's request.
Application
It can be widely used in such applications as sintering and heat treatment of ceramics, magnet, glass, metallurgy, refractory, etc.
Advantage
Mosi2 heating element can quickly form a thin and adhesive anti-oxidizing layer of quartz glass(Sio2), under the high temperature oxidizing condition. If the protective layer was damaged, the element can reform a new one, so Mosi2 heating element has a very good anti-oxidation properties, it also means that the heating element can be used on operation for a much longer time than the traditional one.
The resistivity of the Mosi2 heating element is not changing with the time, so a new one can be installed without effecting the old one, this can result of huge saving in furnace maintenance fee sand time as well, increase the working efficiency, this is the key point of Mosi2 heating element being a better material and being widely used.
Bulk density | Bending strength | Hardness | Apparent porosity | Drawing water rate | Thermal elongation |
5.6~5.8g/cm3 | 20MPa(20ºC) | (hv)570kg/mm² | 0.5~2.0% | 0.5% | 4% |
Furnace Temp(°c) | 1400 | 1500 | 1600 | 1650 | 1700 |
Surface load of hot zone(W/cm²) | <18 | <15 | <12 | <10 | <8 |
Item | name | distinction criterion | specification |
Heating elements |
1700 type | Element operating temperature 1700ºC is acceptable | Le Φ 6-12W type/U type/L type/all kinds of heating element |
1800 type | Element operating temperature 1800ºC is acceptable | ||
1800J type | Element operating temperature≥1800ºC | Le Φ 3-12W type |
|
1800T type | Element operating temperature≤1800ºC | Le Φ 3-12W type U type |
Small furnace (power100KW) | Large furnace(Power 100-500KW) | ||
Furnace temperature | Voltage | furnace temperatureºC | Voltage |
20-150 | 1/3 Operating voltage | 1/3 Operating voltage200-300 | 1/3 Operating voltage |
150-500 | 2/3 Operating voltage | 300-700 | 2/3 Operating voltage |
500-operating temperature | The Whole-Operating Voltage | 700-Operating temperature | The Whole-Operating Voltage |
Suppliers with verified business licenses